| MgO(%): | ≥80 | CaO(%): | ≥4 |
|---|---|---|---|
| Bulk Density (g/cm3): | ≥2.55 | Compressive Strength (MPa): | ≥35 |
| Feature: | Good Fluidity | Application: | Converter |
| High Light: | iron making refractories,high alumina refractory |
||
Good fluidity Self-flowing gunning mass Magnesium refractory for Converter
Self-flowing gunning mass taking the fused magnesia and magnesia-calcium sand as the main raw materials, and the composite carbon and ceramic combination method is used for the heat repair of the converter bottom, large and small surface, slag line and other parts.
Self-flowing gunning mass has the advantages of good fluidity, short sintering time (less than 30 minutes), low smoke pollution and convenient construction.
The hopper is used for feeding and the amount of addition depends on the size of the furnace and the degree of erosion.
| Item | JDZLPB-1 | JDZLPB-2 | JDZLPB-3 | |
|
Chemical content (%) |
MgO ≥ | 80 | 75 | 70 |
| CaO ≥ | 4 | 4.5 | 5 | |
| C ≥ | 5 | 5.5 | 6 | |
| SiO2 ≤ | 4 | 4.5 | 5 | |
| Bulk density (g/cm3) ≥ | 100℃sintering | 2.55 | 2.3 | 2.2 |
| Compressive strength (MPa) ≥ | 100℃sintering | 35 | 30 | 28 |
| Hardening time | ≤ min | 20 | 25 | 30 |
| Flow value | ≥ mm | 200 | 200 | 200 |
| Remark | The specification is just for reference only. The real products will be tailored to special operation conditions and customer’s special requirements. | |||