|Material:||Aluminum-silicon Carbide Refractory Ramming Mass||Bulk Density:||≥2.6|
|SiC Contention (%):||≥75||Size:||Customized|
|Performance:||Corrosion Resistance, Good Thermal Conductivity||Application:||For Filling Different Parts Of The Blast Furnace.|
high alumina refractory,
high temperature refractory
Aluminum-silicon carbide refractory ramming mass good slag resistance
The ramming mass for blast furnace infrastructure is made of silicon carbide, graphite, anthracite, coke and other materials. The phenolic resin, tar or asphalt is used as a binder. After stirring and mixing, it is made into an unshaped refractory material suitable for filling different parts of the blast furnace. It is constructed by ramming method.
1, Good thermal conductivity;
2. Resistance to slag and iron erosion;
3, Resistant to scouring.
Transportation and storage:
1. During the transportation and storage of the ramming materials, they must be noted that the sealed packaging bags should not be damaged to prevent the materials from hardening;
2. If the material inside the package is hard, it can no longer be used.
|Item||Chemical content (%)||Bulk density (g/cm3) ≥||Bending strength (MPa) ≥||Cold crushing strength (MPa) ≥||Linear change rate (%)||Thermal conductivity(w/m·k) ≥|
|JD-SC-3P||SiC≥75 C≤5||2.6||5||--||--||6 (600℃)|
|JD-SN-13P||SiC≥20 C≥40 SiO2≤15 Al2O3≤5||1.8||5||--||±0.8||4 (600℃)|
JD-SC-3P: Ring vertical joint between furnace belly, furnace waist, furnace body and furnace throat cooling wall.
JD-SN-13P: Ring vertical joint between furnace bottom and furnace hearth cooling wall.
JD-BFD-S9: Caulking between furnace bottom and carbon brick masonry of the hearth and the furnace shell.
JD-BFD-S10: Leveling between the furnace bottom water-cooled pipe and furnace bottom floor etc.