Product Details:
Payment & Shipping Terms:
|
AL2O3 Content: | ≥75% | SiO2 Content: | ≤20% |
---|---|---|---|
C.C.S: | ≥80MPa | Bulk Density: | ≥2.60g/cm3 |
Performance: | Thermal Resistant | Application: | Industrial Kiln Lining |
High Light: | kiln fire bricks,refractory kiln lining |
Dense Steel fiber reinforced Castable Refractory unshaped low cement castable for Industrial kiln lining
Steel Fiber Reinforced Castable Refractory is made of special bauxite clinker as aggregate, high quality bauxite clinker and corundum fine powder as matrix, ultrafine powder and other composite materials as binder and additive, plus stainless steel heat-resistant fiber Made. At the same time, due to the addition of steel fibers, the overall strength of the furnace wall after pouring the material is greatly enhanced.
Steel Fiber Reinforced Castable Refractory is applicable to:
1, Masonry high temperature mechanical vibration, thermal shock, wear and other parts.
2, In the steel, metallurgy, chemical and building materials industries are widely used;
3, In the CFB boiler, often used in furnace outlet and side wall, top, cyclone straight section, cyclone top, returner and other parts.
4, The key parts of heat treatment furnaces, heating furnaces, soaking furnaces and other industrial furnaces and thermal equipment, and has obtained good technical and economic results.
How to select the heat-resisting steel fibers used for steel fiber refractory castables?
Firstly weigh the refractory aggregates, powders, binders and admixtures, and dry-mix for one minute; Secondly add water and wet mixing, and evenly spread the steel fibers into the material, and do not clump;
Finally mix for one minute Can be discharged.
The total mixing time must not be less than 5 minutes. When the vibrating rod is used for molding, the vibration direction should be staggered to make the distribution of the steel fiber reasonable, which can improve the performance.
Steel fiber Reinforced Castable Refractory |
Al2O3 (%,Min) |
SiO2 (%,Max) |
Bulk density (g/cm3,Min) |
C.C.S (MPa, Min) | P.L.C (%) |
Water content for construction (%) |
||
110℃*24h dry off | 1100℃*3h burned | 1100℃*3h burned | 1500℃*3h burned | |||||
High-Al GF-15 |
75 | 20 | 2.60 | 80 | 80 | -0.1~0.3 | / | 6~7 |
High-Al GF-16 |
78 | 15 | 2.65 | 100 | 100 | -0.1~0.3 | / | 5.5~6.5 |
Corundum GF-17 | 90 | 6 | 3.00 | 100 | 100 | -0.1~0.3 | ±0.6 | 4.5~5.5 |
Corundum GF-18S |
92 | 4 | 3.00 | 100 | 100 | -0.1~0.3 | ±0.6 | 5~6 |
Remark | ISO Certificated; Customized | |||||||
Application | Cement rotary kiln mouth, cooler, pulverized coal burner and any other industrial kiln lining |
Contact Person: Astra