Product Details:
Payment & Shipping Terms:
|
| Material: | Clay Refractory Mortar | MgO Content: | ≥91% |
|---|---|---|---|
| Bonding Time/min: | 1-3 | Refractoriness/℃: | ≥1680 |
| Performance: | Strong Bonding Strength And Corrosion Resistance | Application: | For Various Industrial Furnaces For High Alumina Brick Masonry. |
| High Light: | high temperature mortar,high heat mortar mix |
||
Magnesia refractory mortar fire clay slurry good plasticity strong bonding strength
Refractory mortar is an amorphous refractory material used as a joint of refractory masonry. It can be divided into clay, high alumina, silica and magnesia refractory mud according to the material.
Characteristic:
1.Good plasticity
2.Convenient construction
3.Strong bonding strength
4.Strong corrosion resistance
5.High refractoriness
6.Good slag resistance
7.Good thermal spalling.
| Item | MN-91 | MN-95 | MN-97 | |
| MgO(%) ≥ | 91 | 95 | 97 | |
| Linear change rate 1500℃×3h(%) | -4~+1 | |||
| Bending strength(MPa)≥ | After drying at 110℃ | 1.5 | ||
| After burning 1500℃×3h | 3.0 | |||
| Granularity(%) | ＜1.0mm | 100 | ||
| ＞0.5mm ≤ | 2 | |||
| ＜0.075mm ≥ | 60 | |||
| Bonding time(min) | 1-3 | |||