| Al2O3/%: | ≥70 | MgO/%: | ≥8 |
|---|---|---|---|
| Bulk Density After Drying （110℃x24h）/MPa / G/cm3: | ≥2.65 | Linear Change Rate After Drying （110℃x24h）/%: | 0～-0.4 |
| Bending Strength After Drying （110℃x24h）/MPa: | ≥7.5 | Cold Crushing Strength After Drying （110℃x24h）/MPa: | ≥30 |
| High Light: | kiln lining materials,castable refractory material |
||
Alumina Magnesia Castable Refractory is a refractory castable prepared by using high alumina bauxite clinker as aggregate, high bauxite clinker powder and magnesia as powder, and sodium water glass as binder. The average age of the package is 60~80 times, and the consumption of refractory material per ton of steel is reduced by about 70% compared with the clay-coated steel.
High Strength Magnesia Ramming Mass Characteristics
1.Excellent chemical stability
2.Good high temperature strength
3.Good thermal shock resistance
4.Good slag resistance
Applications:
It is mainly used for the inner lining of steel drums, ladle and tapping troughs, and has been widely used in the ladle for medium and small die casting.
Aluminum-magnesium refractory castable with characters of high strength, good erosion resistance and excellent thermal shock resistance etc. The most outstanding character is its with good slag resistance, it is because the magnesia powder and high bauxite clinker powder in the castable react under the action of high temperature formed a new mineral: aluminum-magnesium spinel which with high strength, chemical stability and high melting point.
| Brands | LMJ-70 | LMJ-65 | LMJ-60 | |
| Al2O3/% | ≥70 | ≥65 | ≥60 | |
| MgO/% | ≥8 | ≥8 | ≥8 | |
| Bulk density after drying (110℃x24h)/MPa / g/cm3 | ≥2.65 | ≥2.50 | ≥2.40 | |
| Linear change rate after drying (110℃x24h)/% | 0～-0.4 | 0～-0.4 | 0～-0.4 | |
| Bending strength after drying (110℃x24h)/MPa | ≥7.5 | ≥7.5 | ≥7.5 | |
| Cold crushing strength after drying (110℃x24h)/MPa | ≥30 | ≥25 | ≥20 | |
|
Setting time /min |
Initial setting time | ≥45 | ≥45 | ≥45 |
| Final setting time | ≤720 | ≤720 | ≤720 | |
| The highest operating temperature /℃ | 1730 | 1700 | 1680 | |
| Application | Used for integral lining of ladle, hot metal ladle and tapping trough. | |||
Q1: Is Jundao (Henan) New Materials a manufacturer or trader?
A1: Manufacturer, sometimes we help our clients to purchase relevant products as a trader.
Q2: What’s the MOQ?
A2. The MOQ is 25 tons.
Q3: Can we visit your factory?
A3: Of course ,welcome at any time,seeing is believing
Q4: What’s your payment terms?
A4: Negotiation
Q5: Is your company accept customization?
A5: Yes. Professional technology teams and engineers all can satisfy you.
Q6: How do you guarantee quality?
A6: For every production processing,we have complete QC system for the chemical composition and Physical properties.After production,all the goods will be tested ,and the quality certificate will be shipped along with goods.
Q7: Does your Jundao (Henan)?New Materials?supply samples?
A7: Yes, we can supply samples if necessary.
Contact Person: Astra