Product Details:
Payment & Shipping Terms:
|
| AL2O3 Content: | ≥60% | SiO2+SiC Content: | ≥35% |
|---|---|---|---|
| C.C.S: | ≥100MPa | Size: | Customized |
| Performance: | Anti-weat | Application: | Cement Kiln |
| High Light: | fire resistant bricks,boiler fire brick |
||
Cement kiln Silicon Mullite brick, Anti-weat Refractory fire brick Customized
Silicon mullite refractory fire bricks take high bauxite clinker and silicon carbide as the main raw material, it can constantly form protective layer for reducing accrection formation, long application cycle, with normal temperature compressive strength, high temperature structural strength and good thermal shock resistance etc.
Silicon mullite refractory fire bricks Features:
1, High cold crushing strength
2, Good wear resistance, in the use of silicon mullite wear resistant brick it can form a protective layer which has good wear resistant and strong spalling resistance.
3, Thermal shock stability, at 1100℃, thermal shock resistant times is more than 10 times by water cooling.
The prducts are mainly used in cement rotary kiln transition zone, cooling machine, kiln and other parts.
|
Silicon-mullite refractory Brick |
Al2O3 (%,Min) |
Wear resistance |
Bulk density (g/cm3,Min) |
C.C.S (MPa,Min) |
A.P (%,Max) |
R.U.L (℃, Min) |
T.S.R times,Min) |
| GM1 650 | 65 | 5 | 2.65 | 120 | 17 | 1650 | 10 |
| GM1 600 | 63 | 5 | 2.60 | 100 | 17 | 1600 | 10 |
| GM1 550 | 60 | 5 | 2.55 | 100 | 19 | 1550 | 12 |
| Remark | ISO Certificated; Customized | ||||||
| Application | Cement rotary kiln transition zone, cooler and other parts | ||||||