| Al2O3/% ≥: | 65 | SiC，% ≥: | 10 |
|---|---|---|---|
| C，% ≥: | 10 | Apparent Porosity，% ≤: | 8 |
| Bulk Density，g/cm3 ≥: | 2.85 | Cold Crushing Strength，Mpa≥: | 50 |
| High Light: | fire retardant bricks,boiler fire brick |
||
Aluminum carbide silicon carbon brick for torpedo ladle
The main raw material of aluminum carbide carbon brick for hot metal ladle is electrofusion corundum (or sintered corundum and special bauxite clinker) and graphite and SiC with fixed carbon over 90%-95%, by adding graphite, bauxite, additive, then made by mixing, pressing, drying, burning at high temperature.
The main raw material of aluminum carbide carbon brick for hot metal ladle is electrofusion corundum (or sintered corundum and special bauxite clinker) and graphite and SiC with fixed carbon over 90%-95%, by adding graphite, bauxite, additive, then made by mixing, pressing, drying, burning at high temperature.
Aluminum carbide carbon brick is a refractory product for the working layer of torpedo ladle.
Features:
1. Suitable brick type and easy to build.
2. Good thermal shock resistance
3. High strength and resistant to corrosion of mechanical strength and good wear resistance.
4. Good corrosion resistance of slag.
5. Micro-expansion is produced in high temperature, extruding brick seam and has the good overall performance.
| Band | Aluminum carbide carbon brick | ||
| ASC-1 | ASC-2 | ASC-P1 | |
| Al2O3,% ≥ | 65 | 60 | 55 |
| SiC,% ≥ | 10 | 8 | 8 |
| C,% ≥ | 10 | 12 | 5 |
| Apparent Porosity,% ≤ | 8 | 8 | 9 |
| Bulk density,g/cm3 ≥ | 2.85 | 2.83 | 2.80 |
| Cold crushing strength,Mpa≥ | 50 | 50 | 45 |
| Bending Strength In High Temperature,Mpa(1400℃X0.5h)≥ | 8 | 7 | 5 |
| Part Used | Impact area | Slag line area and the top | Hot metal region |
Aluminum carbide silicon carbon based resin bonded bricks have been finding increasing applications in the field of hot metal pretreatment process in torpedo ladle worldwide. In the pretreatment process in the steel ladles, refractories are subjected to very stringent demand of performance. This process helps in the production of quality steel and is the most popular process. The alumina-silicon carbide-carbon based refractories are suitable for the torpedo ladle as they have the best slag penetration resistance and are thus suitable for slag zone and bottom impact zone of steel ladle.
There are 7 grades of aluminum carbide carbon bricks for torpedo ladle. Different areas use different grades of firebrick. If you'd like more information of aluminum carbide silicon carbon brick for torpedo ladle, please contact us. Jundao is a professional manufacturer of refractories, which can provide customer with all kinds of refractory materials for iron making, steel making and contract service.
Q1: Is Jundao (Henan) New Materials a manufacturer or trader?
A1: Manufacturer, sometimes we help our clients to purchase relevant products as a trader.
Q2: What’s the MOQ?
A2. The MOQ is 25 tons.
Q3: Can we visit your factory?
A3: Of course ,welcome at any time,seeing is believing
Q4: What’s your payment terms?
A4: Negotiation
Q5: Is your company accept customization?
A5: Yes. Professional technology teams and engineers all can satisfy you.
Q6: How do you guarantee quality?
A6: For every production processing,we have complete QC system for the chemical composition and Physical properties.After production,all the goods will be tested ,and the quality certificate will be shipped along with goods.
Q7: Does your Jundao (Henan)?New Materials?supply samples?
A7: Yes, we can supply samples if necessary.
Contact Person: Astra